沙伯基础SABIC LEXAN PC EXL1890T 注射成型、食品级。易脱模、高流动、加工性能良好。
LEXAN™ EXL1890T resin
聚碳酸酯PC
SABIC Innovative Plastics Asia Pacific
PC EXL1890T 产品说明:
LEXAN EXL1890T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade for food contact applications. This resin offers cold temperature (0 °C) ductility in combination with very high flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC resin. LEXAN EXL1890T resin offers enhanced release performance and is available in transparent colors and is an excellent candidate for a broad range of applications in food handling or food preparation markets.
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 比重 | 1.19 | g/cm³ | ASTM D792, ISO 1183 |
| 熔流率（熔体流动速率） (300°C/1.2 kg) | 35 | g/10 min | ASTM D1238 |
| 溶化体积流率（MVR） (300°C/1.2 kg) | 33.0 | cm³/10min | ISO 1133 |
| 收缩率 | 内部方法 | ||
| 流动 : 3.20 mm | 0.40 到 0.80 | % | |
| 横向流动 : 3.20 mm | 0.40 到 0.80 | % | |
| 吸水率 | ISO 62 | ||
| 饱和, 23°C | 0.12 | % | |
| 平衡, 23°C, 50% RH | 0.093 | % | |
| 硬度 | 额定值 | 单位制 | 测试方法 |
| 洛氏硬度 (L 计秤) | 90 | ASTM D785 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 拉伸模量 | |||
| -- 2 | 2370 | MPa | ASTM D638 |
| -- | 2400 | MPa | ISO 527-2/1 |
| 抗张强度 | |||
| 屈服 3 | 60.0 | MPa | ASTM D638 |
| 屈服 | 59.0 | MPa | ISO 527-2/50 |
| 断裂 3 | 58.0 | MPa | ASTM D638 |
| 断裂 | 56.6 | MPa | ISO 527-2/50 |
| 伸长率 | |||
| 屈服 3 | 5.8 | % | ASTM D638 |
| 屈服 | 5.4 | % | ISO 527-2/50 |
| 断裂 3 | 120 | % | ASTM D638 |
| 断裂 | 120 | % | ISO 527-2/50 |
| 弯曲模量 | |||
| 50.0 mm 跨距 4 | 2360 | MPa | ASTM D790 |
| -- 5 | 2250 | MPa | ISO 178 |
| 弯曲应力 | |||
| -- 5, 6 | 92.9 | MPa | ISO 178 |
| 屈服, 50.0 mm 跨距 4 | 99.2 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度 7 | ISO 179/1eA | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 65 | kJ/m² | |
| 简支梁无缺口冲击强度 7 | ISO 179/1eU | ||
| -30°C | 无断裂 | ||
| 23°C | 无断裂 | ||
| 悬壁梁缺口冲击强度 | |||
| -30°C | 220 | J/m | ASTM D256 |
| 23°C | 700 | J/m | ASTM D256 |
| -30°C 8 | 30 | kJ/m² | ISO 180/1A |
| 23°C 8 | 60 | kJ/m² | ISO 180/1A |
| 无缺口伊佐德冲击强度 8 | ISO 180/1U | ||
| -30°C | 无断裂 | ||
| 23°C | 无断裂 | ||
| 装有测量仪表的落镖冲击 (23°C, Total Energy) | 79.0 | J | ASTM D3763 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 载荷下热变形温度 | |||
| 1.8 MPa, 未退火, 3.20 mm | 121 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 64.0 mm 跨距 9 | 118 | °C | ISO 75-2/Af |
| 维卡软化温度 | |||
| -- | 138 | °C | ASTM D1525 10, ISO 306/B50 10 |
| -- | 140 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | 通过 | IEC 60695-10-2 | |
| 线形热膨胀系数 | |||
| 流动 : -40 到 95°C | 6.5E-5 | cm/cm/°C | ASTM E831 |
| 流动 : 23 到 80°C | 6.5E-5 | cm/cm/°C | ISO 11359-2 |
| 横向 : -40 到 95°C | 7.4E-5 | cm/cm/°C | ASTM E831 |
| 横向 : 23 到 80°C | 7.4E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 130 | °C | UL 746 |
| RTI | 130 | °C | UL 746 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
| 表面电阻率 | > 1.0E+15 | ohms | ASTM D257 |
| 体积电阻率 | > 1.0E+15 | ohms·cm | ASTM D257 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
| UL 阻燃等级 (1.5 mm) | HB | UL 94 | |
| 灼热丝易燃指数 (3.0 mm) | 960 | °C | IEC 60695-2-12 |
| 热灯丝点火温度 | IEC 60695-2-13 | ||
| 0.8 mm | 825 | °C | |
| 3.0 mm | 850 | °C |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
| 透射率 (2540 µm) | 82.0 | % | ASTM D1003 |
| 雾度 (2540 µm) | 3.0 | % | ASTM D1003 |
| 注射 | 额定值 | 单位制 | |
| 干燥温度 | 121 | °C | |
| 干燥时间 | 3.0 到 4.0 | hr | |
| 干燥时间，最大 | 48 | hr | |
| 建议的最大水分含量 | 0.020 | % | |
| 建议注射量 | 40 到 60 | % | |
| 料筒后部温度 | 217 到 293 | °C | |
| 料筒中部温度 | 282 到 304 | °C | |
| 料筒前部温度 | 293 到 316 | °C | |
| 射嘴温度 | 288 到 310 | °C | |
| 加工（熔体）温度 | 293 到 316 | °C | |
| 模具温度 | 71.0 到 93.0 | °C | |
| 背压 | 0.345 到 0.689 | MPa | |
| 螺杆转速 | 40 到 70 | rpm | |
| 排气孔深度 | 0.025 到 0.076 | mm |
沙伯基础SABIC LEXAN PC EXL1890T 注射成型、食品级。易脱模、高流动、加工性能良好。以上是沙伯基础SABIC LEXAN PC EXL1890T物性数据。如需了解沙伯基础SABIC LEXAN PC EXL1890T单价、交期或其它塑胶原料信息请联系我们！